Reprocessed and Virgin PVC Compounds



SPECIFICATIONS

We have a wide range of reprocessed PVC compounds and virgin PVC compounds for many industries.
Please note than only some of specifications have been tabled here and a lot more can be customized.All kind of customised modifications are possible


PVC CRYSTAL COMPOUNDS,
PVC CRYSTAL DANA,
PVC CRYSTAL GRANULES

Responsive Table Example
CHARACTERISTICS UNITS TEST METHODS PVC CRYSTAL COMPOUND
shade transparent natural
specific gravity ASTM D-792 1.28
shore A hardness shore A ASTM D-2240 95
tensile strength kg/cm2 IS:2076 M/D-220, T/D-205
elongation % IS:2076 M/D-280, T/D-240
tear strength kg/cm IS:2076 M/D-55, T/D-60
ash content at 800°C for 2 hours % IS:4669 0.068
volatile loss at 120°C for 24 hours % IS:3464 9.5
use for topping/insulating mat/railway hrr

PVC COMPOUND (Beige colour),
PVC DANA (Beige colour),
PVC GRANULE (Beige colour)

CHARACTERISTICS UNITS TEST METHODS BEIGE
shade BEIGE
specific gravity A5TM 0-792 1.47
shore A hardness shore A A5TM 0-2240 80
tensile strength kg/cm2 15:2076 M/0-134 IT/0-122
elongation % 15:2076 M/0-276, T/0-280
tear strength kg/cm 15:2076 M/0-26.4, T/0-34.4
ash content at 800°C for 2 hours % 15:4669 12%
volatile loss at 120°C for 24 hours % 15:3464
use for flooring mat/ut

PVC GLUCOSE COMPOUNDS,
PVC GLUCOSE DANA,
PVC GLUCOSE GRANULES

CHARACTERISTICS UNITS TEST METHODS GLUCOSE
shade opaque/clear
specific gravity A5TM 0-792 1.22
shore A hardness shore A A5TM 0-2240 85
tensile strength kg/cm2 15:2076 M/0-157, T/0-146
elongation % 15:2076 M/0-255, T/0-260
tear strength kg/cm 15:2076 M/0-41, T/0-43
ash content at 800°C for 2 hours % 15:4669 0.043
volatile loss at 120°C for 24 hours % 15:3464 7.4
use for railway ot/insulating mat

PVC BK-41 BLACK COMPOUNDS,
PVC BK-41 BLACK DANA,
PVC BK-41 BLACK GRANULES

Responsive Table Example
CHARACTERISTICS UNITS TEST METHODS BK-41
shade black
specific gravity A5TM 0-792 1.63
shore A hardness shore A A5TM 0-2240 80
tensile strength kg/cm2 15:2076 M/0-100, T/0-98
elongation % 15:2076 M/0-210, T/0-250
tear strength kg/cm 15:2076 M/0-9.7, T/0-14.9
ash content at 800°C for 2 hours % 15:4669 24
volatile loss at 120°C for 24 hours % 15:3464 14
use for tata ace

PVC ST1 , ST2 , RDSO COMPOUNDS,
PVC ST1 , ST2 , RDSO DANA,
PVC ST1 , ST2 , RDSO GRANULES

CHARACTERISTICS STl STZ ROSO
Grade Name As Per IS 5831 STl ST2 ROSO
Gravity/density 1.52(+/-0.02) 1.52(+/-0.02) 1.45(+/-0.02)
Tensile Strength N/m m2 15 15 17.5
Elongation At Break % 200 200 250
Thermal Stability @ 200°C (2 hours) 70 90 100
Hardness Shore A 90(+/-3) 92(+/-3) 90(+/-3)
Maximum Operating Temp. °C 70 90 100
Ageing Temperature °C 80 100 80
Duration of Ageing hours 168 168 168
Variation of Tensile Strength % (+/-) 20 20 20
Variation of Elongation % (+/-) 20 20 20
Loss of Mass mg/cm2 max. 2 2 2
Use For PVC insulation and sheath of electric cables